Gypsum hand plaster

Gypsum based hand plasters are used for smaller areas as well as during renovation. They are stirred either by hand or with a machine and applied manually, usually with a trowel. Gypsum based hand or bonding plasters are less delayed than gypsum based machine plasters.

To keep shrinkage to a minimum, unmodified Tylose® MC types are recommended. Tylose® prevents excessive absorption of water into the substrate or the ceramic covering, giving enough time for rubbing and finishing.

Tylose Grades Product Characteristic Fact Sheet
MH 60010 P4 Final consistency :high » Read more
MO 30023 P4 Final consistency :high » Read more

Building materials

Tylose® is an essential component in many building materials. It is mainly responsible for water retention, consistency and adhesion. The homogeneity, stability and workability of mortars are improved by the use of Tylose®. Using Tylose® enables the manufacturing of modern and efficient construction materials, such as machine plasters and thin bed adhesives.

Nomenclature Information
Type of ether Viscosity level Chemical refinement
M Methyl 60000

The viscosity level

is based on

Hoeppler: 2%

solution of the

commercial product

with 5% moisture

content, 20ºC,

20º dH

(German hardness)

Y Delayed solubility products
H Hydroxyethyl 30000 K Readily soluble granules
O Hydroxypropyl 15000 N non-delayed solubility products
A Allyl 10000 (only for Tylose H grades) *
X Hydrophobe 6000
etherification 4000 Degree of particle size
2000 Types of granules:
Degree of 1000 G4 Granules (< 500 μm)
B etherification 300 G6 Granules (< 400 μm)
F Special higher 200 G6 Granules (< 400 μm)
S degrees of . Powder types:
T etherification, . P2 Powder (< 180 μm)
depending on the . P3 Fine Powder (< 125 μm)
individual type of 01 P4 Fine powder (< 125 μm)
ether 02 P6 Ultra fine powder (< 100 μm)
03
04
.
.
.

* Tylose MH and MO Grades are not explicitly marked by ”N”, even if these products are ”non-delayed solubility products”.